90/28 PP PE peletização de cilindro de extrusão de parafuso
$3800- /Set/Sets
Quantidade de pedido mínimo: | 1 Set/Sets |
$3800- /Set/Sets
Quantidade de pedido mínimo: | 1 Set/Sets |
Brand Name: Batten
Process: Nitriding & Bimetallic
Hardening Hardness: Hb280-320
NITRIDED HARDNESS: Hv900-1000
Nitrided Case Depth: 0.45-0.8mm
Nitrided Brittleness: Less Than Grade 2
Surface Roughness: Ra 0.4
Screw Straightness: 0.015mm
Guarantee: One Year
Application: Single Screw And Barrel Plastic Extruder Machinery
Place Of Origin: Zhejiang, China
Material: 38crmoala
Unidades de venda | : | Set/Sets |
Parâmetro:
Modelo: 90/28
Nome: cilindro de rosca de peletização para PP, PE
Garantia: Um ano
Zona de aquecimento do barril: 4 zonas
Velocidade: 60 ~ 90rpm / h
Especificação técnica
* Também podemos fazer barris de parafuso para atender a sua solicitação especial *
Base materials |
1.38CrMoAla(JIS SACM645) |
Alloy |
1.Ni-based alloy/Deloro Stellite |
2.SKD61 |
2.Tungsten carbide/Wolfram carbide |
||
3.42CrMo(JIS SACM440) |
3.NiCo-based alloy Stellite |
||
4.DC53 |
4.Fe-based alloy |
||
5.W6Mo5Cr4v2 |
5.Co-based alloy |
||
Processing Technical |
1.Heat-treatment |
Inspection Standard |
1.Hardness After Hardening & Tempering:HB280-320 |
2.Nitriding treatment |
2.Nitrided Hardness:HV900-1000 |
||
3.Electroplated hard-chrome plating finish |
3.Nitrided Case Depth:0.45-0.8mm |
||
4.High frequency quenching |
4.Nitrided Brittleness: Less than Grade 2 |
||
5.Spay bimetallic coating(PTA) |
5.Surface Roughness: Ra 0.4 Ra≤1.6μm |
||
6.Vaccum quenching |
6.Screw Straightness:0.015mm |
||
7.centrifugal casting for barrel |
7.Alloy Hardness:HRC 50-65 |
||
8.Blackening |
8.Alloy Depth:0.8-2.0mm |
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.